Changes in Implant Surface Characteristics and Wettability Induced by Smoking In Vitro: A Preliminary Investigation

The biologic response following the insertion of dental implants is a widely studied process. Recent research has highlighted the importance of implant surface topography and chemistry as highly influential factors in consolidating the dental implant with the surrounding biological environment. The hydrophilicity, or wettability, of dental implants plays a pivotal role in these interactions and successful osseointegration. A more well-established factor that can also influence the development of the tissue–implant interface is exposure to tobacco smoke. While the negative impact of smoking on the biological response of the tissue is clear, there has been no research evaluating the impact that tobacco smoke can have directly on the surface chemistry of dental implants. The present study aimed to explore the effect of smoking on implant surface chemistry and wettability in vitro. Five different implant disks (Ti-Mach, Ti-SLA, Ti-Alloy, Zirc-1 and Zirc-2) were subjected to contamination with tobacco smoke using a portable smoke infuser with dome enclosure. Occasional smoking (5×/day 10 min each for 3 days) and heavy smoking (20×/day for 10 min each for 10 days) were simulated. The wettability of the implant disks was evaluated via the contact angle technique using artificial blood and albumin, as well as saline as a control. It was determined that the contamination of implant surfaces due to smoking produces changes in the surface chemistry and wettability. Changes in the surface hydrophilicity differed based on the implant material. Within the constraints of this investigation, tobacco smoke improved the hydrophilicity of titanium surfaces but worsened that of ceramic surfaces when utilizing the testing solutions. Different implant surfaces exhibit different wetting behavior following contamination with nicotine smoke. This might have an impact on the treatment of peri-implantitis in smokers due to changes in implant surface hydrophilicity, which can affect the re-osseointegration process.