How strain affects the reactivity of surface metal oxide catalysts

Highly dispersed molybdenum oxide supported on mesoporous silica SBA-15 has been prepared by anion exchange resulting in a series of catalysts with changing Mo densities (0.2-2.5 Mo atoms nm^-2). X-ray absorption, UV/Vis, Raman, and IR spectroscopy indicate that doubly anchored tetrahedral dioxo MoO₄ units are the major surface species at all loadings. Higher reducibility at loadings close to the monolayer measured by temperature-programmed reduction and a steep increase in the catalytic activity observed in metathesis of propene and oxidative dehydrogenation of propane at 8 % of Mo loading are attributed to frustration of Mo oxide surface species and lateral interactions. Based on DFT calculations, NEXAFS spectra at the O-K-edge at high Mo loadings are explained by distorted MoO₄ complexes. Limited availability of anchor silanol groups at high loadings forces the MoO₄ groups to form more strained configurations. The occurrence of strain is linked to the increase in reactivity. Only uncomfortable seats left: At high surface coverages of molybdenum oxide, at which surface hydroxy anchoring sites are limited, surface metal oxide molecules are forced to be anchored in strained/frustrated configurations. This strain leads to increased reactivity and explains the non-linear coverage dependence sometimes observed in monolayer-type supported metal oxide catalysts.