MODIFICATION OF THE CORROSION BEHAVIOR OF 304 STAINLESS STEEL BY PHOSPHORUS IMPLANTATION.

C. R. Clayton; K. G.K. Doss; H. Herman; S. Prasad; Y. F. Wang; J. K. Hirvonen; G. K. Hubler

MODIFICATION OF THE CORROSION BEHAVIOR OF 304 STAINLESS STEEL BY PHOSPHORUS IMPLANTATION.

C. R. Clayton
, K. G.K. Doss
, H. Herman
, S. Prasad
, Y. F. Wang
, J. K. Hirvonen
, G. K. Hubler

Materials Science and Engineering

Research output: Contribution to conference › Paper › peer-review

Abstract

Phosphorus was implanted into 304 stainless steel at a fluence of 10**1**7 ions cm** minus **2 at 40 KeV. The structure of the surface alloy formed was microcrystalline, with P in solid solution. The modification of corrosion behavior was determined from electrochemical polarization experiments carried out in deaerated lN H//2SO//4 and 0. 1 M NaCl solution. ESCA was used to characterize the composition and relative thickness of the passive film formed at plus 550 mV.

Original language	English
Pages	65-76
Number of pages	12
State	Published - 1980
Event	Ion Implantation Metall, Proc of a Symp at Annu Meet of the Mater Res Soc - Cambridge, MA, Engl Duration: Nov 30 1979 → Nov 30 1979

Conference

Conference	Ion Implantation Metall, Proc of a Symp at Annu Meet of the Mater Res Soc
City	Cambridge, MA, Engl
Period	11/30/79 → 11/30/79

Cite this

@conference{814c5b82bbf445febb52035084d0dab9,

title = "MODIFICATION OF THE CORROSION BEHAVIOR OF 304 STAINLESS STEEL BY PHOSPHORUS IMPLANTATION.",

abstract = "Phosphorus was implanted into 304 stainless steel at a fluence of 10**1**7 ions cm** minus **2 at 40 KeV. The structure of the surface alloy formed was microcrystalline, with P in solid solution. The modification of corrosion behavior was determined from electrochemical polarization experiments carried out in deaerated lN H//2SO//4 and 0. 1 M NaCl solution. ESCA was used to characterize the composition and relative thickness of the passive film formed at plus 550 mV.",

author = "Clayton, \{C. R.\} and Doss, \{K. G.K.\} and H. Herman and S. Prasad and Wang, \{Y. F.\} and Hirvonen, \{J. K.\} and Hubler, \{G. K.\}",

year = "1980",

language = "English",

pages = "65--76",

note = "Ion Implantation Metall, Proc of a Symp at Annu Meet of the Mater Res Soc ; Conference date: 30-11-1979 Through 30-11-1979",

}

TY - CONF

T1 - MODIFICATION OF THE CORROSION BEHAVIOR OF 304 STAINLESS STEEL BY PHOSPHORUS IMPLANTATION.

AU - Clayton, C. R.

AU - Doss, K. G.K.

AU - Herman, H.

AU - Prasad, S.

AU - Wang, Y. F.

AU - Hirvonen, J. K.

AU - Hubler, G. K.

PY - 1980

Y1 - 1980

N2 - Phosphorus was implanted into 304 stainless steel at a fluence of 10**1**7 ions cm** minus **2 at 40 KeV. The structure of the surface alloy formed was microcrystalline, with P in solid solution. The modification of corrosion behavior was determined from electrochemical polarization experiments carried out in deaerated lN H//2SO//4 and 0. 1 M NaCl solution. ESCA was used to characterize the composition and relative thickness of the passive film formed at plus 550 mV.

AB - Phosphorus was implanted into 304 stainless steel at a fluence of 10**1**7 ions cm** minus **2 at 40 KeV. The structure of the surface alloy formed was microcrystalline, with P in solid solution. The modification of corrosion behavior was determined from electrochemical polarization experiments carried out in deaerated lN H//2SO//4 and 0. 1 M NaCl solution. ESCA was used to characterize the composition and relative thickness of the passive film formed at plus 550 mV.

UR - https://www.scopus.com/pages/publications/0019279814

M3 - Paper

AN - SCOPUS:0019279814

SP - 65

EP - 76

T2 - Ion Implantation Metall, Proc of a Symp at Annu Meet of the Mater Res Soc

Y2 - 30 November 1979 through 30 November 1979

ER -

MODIFICATION OF THE CORROSION BEHAVIOR OF 304 STAINLESS STEEL BY PHOSPHORUS IMPLANTATION.

Abstract

Conference

Other files and links

Fingerprint

Cite this