Perovskite evolution on La modified Mn_1.5Co_1.5O₄ spinel through thermal ageing with enhanced oxidation activity: Is sintering always an issue?

Non-precious metal oxides have great potential in catalytic deep oxidation of emitted hydrocarbons to help address various environmental pollution concerns. However, sintering issue is a stumbling block in practical application upon long-term high-temperature operation or thermal shock experience. Herein, La was applied to modify Mn_1.5Co_1.5O₄ spinel to get a highly active oxidation catalyst with exceptional stability against high-temperature thermal ageing treatment. With thermal ageing at 750 °C for 100 h, the La modified Mn–Co composite reached 90 % conversion in toluene oxidation at 265 °C under the high WHSV of 120,000 mL g⁻¹ h⁻¹, while this value increased to 312 °C over blank Mn–Co spinel. The addition of La not only inhibited the growth of spinel nanocrystals, but also brought about perovskite formation through sintering, generating perovskite-spinel interfaces, thus enhancing both activity and stability. Meanwhile, the La modified Mn–Co spinel exhibited superior performance in presence of water or sulfur dioxide after thermal ageing treatment. This work offers a versatile strategy to design anti-sintering and active oxidation nanocatalysts based on non-precious metal oxides for industrial applications.