²⁷Al, ²⁹Si, and ²³Na MAS NMR study of an Al, Si ordered alkali feldspar solid solution series

Solid-state ²⁷Al, ²⁹Si and ²³Na MAS NMR spectra have been obtained for an Al,Si ordered low albite to low microcline ion exchange series for which unit-cell parameters and ²⁹Si NMR data have previously been reported. ²⁷Al δ_i vary continuously with composition from 63.4 (±0.5) ppm for albite to 58.9 (±0.5) ppm for microcline, and parallel the ²⁹Si chemical shifts assigned to the T2m-site. The ²⁷Al and ²⁹Si chemical shifts for this series correlate well with composition-dependent lattice parameters, most notably cell volume and the angle [201]¹b. The linewidths of the ²⁹Si and ²⁷Al resonances indicate a significant amount of structural disorder in the intermediate compositions due to Na, K substitution. The 1 σ width of the distribution of average Si-O-T angles for each T-site is estimated to be about 1° for the Or33 sample. The average ²³Na δ_i varies monotonically from -8.5 (±1) ppm for albite to -24.3 (±1)ppm for Or83. Similarly, the average ²³Na nuclear quadrupole coupling constant decreases from 2.60 to 1.15 (±0.05) MHz and the asymmetry parameter of the electric field gradient increases from 0.25 to 0.6 with increasing K-content from albite to Or83. The observed variations in the quadrupole coupling parameters are consistent with simple electrostatic calculations. Higher resolution ²³Na spectra of the intermediate compositions obtained at 11.7 T indicate the presence of an inhomogeneous linebroadening which is related to the distribution of Na-environments. A model based on a random distribution of local compositions does not simulate the spectra, suggesting that the distribution of Na is skewed toward Na-rich clusters. Observation of the ²³Na NMR lineshape of Or49 after short periods of heat treatment indicate that ²³Na NMR is very sensitive to the changes in the Na, K distribution accompanying the early stages of exsolution. Reversible changes occur after heating at 530° C for 3 h, whereas heating at 600° C produces no changes, possibly bracketing the position of the coherent spinodal for Al, Si ordered alkali feldspars at this composition.