The nature of ordering and ordering defects in dolomite

The apparent lack of transformation-induced domains and stacking disorder defects in natural dolomites is considered in light of the different types of order in the dolomite structure. Experimentally produced twin domain boundaries and basal stacking defects are documented in a dolomite using high-resolution electron microscopy and electron diffraction techniques. Results reveal that upon cation ordering to form the dolomite structure, a twin domain is favored over an antiphase domain. The twin domain boundaries closely resemble antiphase boundaries (APB's) and are in contrast for superlattice reflections. However, background contrast within domains is shown to be different when imaged using certain fundamental reflections. The results allow speculation about the nature of ordering at low temperatures. Observations of twin domain boundaries in samples annealed at different temperatures allow estimation of the critical ordering temperature at 1,100°-1,150° C in stoichiometric dolomite.