Understanding coarsening of a post-corrosion microstructure in a molten salt by combining phase-field modeling and in situ tomography

Alloys corroding in molten salt have been observed to form bicontinuous, nanoporous microstructures via dealloying, which subsequently undergo coarsening due to facile transport in high-temperature conditions. In this work, we describe a methodology to elucidate the underlying transport mechanisms during coarsening of a bicontinuous microstructure via quantitative comparisons between phase-field simulations and four-dimensional in situ experiments, in this case X-ray nanotomography of the coarsening of a dealloyed 80 wt% Ni-20 wt% Cr microwire in molten KCl-MgCl₂ at 800°C. We conduct phase-field simulations initialized from experimental data to model coarsening via three different transport mechanisms: surface diffusion, solid bulk diffusion, and liquid bulk diffusion. These simulations reproduce key features of the experiment, such as the densification of the outer layer of the dealloyed wire and the reduction in radius over time. We quantitatively compare different microstructural characteristics between the simulations and experiment and extract temporal scaling factors that optimally match the time scales of the simulations to that of the experiment. This allows us to evaluate morphological similarity between the simulations and experiment and relate the experimental coarsening kinetics to fundamental material properties. We find that surface diffusion is most likely to be the dominant coarsening mechanism, and its kinetics imply a surface diffusivity of D_S=8.9×10⁻²⁰m³/s, which is within the range of reported values for Ni-vacuum interfaces at 800°C. However, the difference between the experiment and the surface diffusion simulation increases substantially at late times, suggesting that other mechanisms, such as the dissolution of residual Cr, may be at play.